Jen-Radiance Molar (Jen Radiance Molar) syringe 4 g U

INSTRUCTIONS FOR USE

• As a base layer of composite material for direct restorations of classes I and II.
• Sandwich technique.
• Restoring the stump.

ADVANTAGES

• The high content of the material (82%) is due to the new formula of the bimodal filler with an average particle size:
  • the main radiopaque phase - up to 8 μm;
  • nanophase – 10 – 30 nm (nanometers).
• Compatible and perfectly combined with all types of opaque and enamel composite materials based on methacrylates, intended for aesthetic modeling of enamel surfaces of teeth.
• Low polymerization shrinkage (less than 1.63%), which is especially important when filling large cavities in one go.
• Excellent manual qualities - the material is plastic and does not stick to the tool.
• The coefficient of thermal expansion (CTE) is as close as possible to tooth tissue - 24x10 - 6 cm/cm ^o C, which causes the absence of thermal stresses in restored teeth that occur during eating ("hot-cold").
• High physical characteristics of the material, in particular:
  • bending strength – 140 MPa;
  • compressive strength - 340 MPa.
• It is produced in the universal transparent shade U to ensure the maximum depth of polymerization.
• The non-photopolymerized material has increased resistance to natural and artificial lighting, which allows for long-term modeling without the risk of premature polymerization of the material.
• The material is radiopaque and contains fluorine.